PT  - JOURNAL ARTICLE
AU  - Wang, Haibo
AU  - Wang, Dongpo
AU  - Cheng, Fangjie
AU  - Deng, Caiyan
AU  - Wu, Yunlong
TI  - Study on Q245 Steel fatigue crack growth behaviors at high temperature
DP  - 2014 Dec 1
TA  - Manufacturing Technology Journal
PG  - 637--643
VI  - 14
IP  - 4
AID - 10.21062/ujep/x.2014/a/1213-2489/MT/14/4/637
IS  - 12132489
AB  - Q245 steel was once widely used in the pressure vessel industry.At present, the high temperature fatigue performance of Q245 steel was tested and analyzed. According to the relevant standards, the pre-crack specimens were tested at 25℃and400℃respectively. The a-N curves, the da / dN  K curves and the Paris formula of Q245 steelat both room temperature(25℃) and high temperature(400℃) were obtained. Finally,the high temperature fatigue fracture analysis was done.The fatigue crack growth occurredalong the grain at high temperature. A large number of acicular oxideappearin the fracture surface and the fatigue striations could notbe observed at high temperature.