TI Influence of High-Pressure Die-Casting Second Stage Parameter on Structure Of AlSi9Cu3(Fe) Alloy
SO Manufacturing Technology Journal
PY 2016
BP 410
EP 416
VL 16
IS 2
DI 10.21062/ujep/x.2016/a/1213-2489/MT/16/2/410
DE pressure die casting; structure; silumin; SEM; 2nd injection stage
AB In the paper, results of a research on influence of piston stroke rate on structures of AlSi9Cu3(Fe) (EN AB-46000 group) castings manufactured at constant intensification pressure of 290 bar are presented. Relation between piston speed (0.3-2.3 m/s) and casting structure was evaluated after a series of trial high-pressure castings. The examinations were carried-out on properly prepared samples taken from the castings in places with the largest cross-section area. The effect of pouring rate was evaluated on the grounds of metallographic observations on a light microscope and a scanning electron microscope. It was found that larger grains of the very hard phase solidify at low piston speed between 0.3 and 0.75 m/s. Higher piston speed results in finer casting structure and in refinement of particles of intermetallic Fe-Mn phase, which is beneficial for usable properties of the castings.
ER