TI  - Influence of High-Pressure Die-Casting Second Stage Parameter on Structure Of AlSi9Cu3(Fe) Alloy
DP  - 2016 Apr 1
TA  - Manufacturing Technology Journal
PG  - 410--416
VI  - 16
IP  - 2
AID - 10.21062/ujep/x.2016/a/1213-2489/MT/16/2/410
IS  - 12132489
AB  - In the paper, results of a research on influence of piston stroke rate on structures of AlSi9Cu3(Fe) (EN AB-46000 group) castings manufactured at constant intensification pressure of 290 bar are presented. Relation between piston speed (0.3-2.3 m/s) and casting structure was evaluated after a series of trial high-pressure castings. The examinations were carried-out on properly prepared samples taken from the castings in places with the largest cross-section area. The effect of pouring rate was evaluated on the grounds of metallographic observations on a light microscope and a scanning electron microscope. It was found that larger grains of the very hard phase solidify at low piston speed between 0.3 and 0.75 m/s. Higher piston speed results in finer casting structure and in refinement of particles of intermetallic Fe-Mn phase, which is beneficial for usable properties of the castings.