PT  - JOURNAL ARTICLE
AU  - Kučera, Vojtěch
AU  - Průša, Filip
AU  - Vojtěch, Dalibor
TI  - Processing of Al-Fe Scraps by Powder Metallurgy
DP  - 2016 Aug 1
TA  - Manufacturing Technology Journal
PG  - 726--732
VI  - 16
IP  - 4
AID - 10.21062/ujep/x.2016/a/1213-2489/MT/16/4/726
IS  - 12132489
AB  - Iron has a low solubility in aluminium solid solution even at elevated temperatures and forms brittle intermetallic phases with needle-like or platelets-like morphology when it is produced by conventional casting technologies. These phases have a detrimental effect on mechanical properties. Therefore with increasing significance of recycling and also amount of aluminium scrap that needs to be recycled, it is necessary to find a promising ways of processing such waste materials. Powder metalurgy leads to intensive microstructural refinement, increases solid solubility of alloying elements and overall to improvement of mechanical properties. Hence, it belongs to promising alternatives for proccesing aluminium materials with increased amount of iron. Aluminium alloy with 17 wt. % iron was prepared by centrifugal atomization and consolidated by spark plasma sintering followed by hot extrusion. The microstructure and phase composition of compact samples as well as mechanical properties were studied. Fine microstructure has been achieved by centrifugal atomization and consolidation by spark plasma sintering in combination with hot extrusion. Compression strength was 565 MPa with remarkable ductility reaching almost 35 %.