T1 Microstructure and Fatigue Properties of Nodular Cast Iron at Low Frequency Cyclic Loading
JF Manufacturing Technology Journal
YR 2016
VO 16
IS 5
SP 1188
OP 1193
DO 10.21062/ujep/x.2016/a/1213-2489/MT/16/5/1188
UL https://journalmt.com/artkey/mft-201605-0065.php
AB The paper deals with the influence of charge composition on microstructure, mechanical and fatigue properties of synthetic nodular cast irons and their micromechanisms of failure. The basic charge of experimental melts was formed by a different ratio of pig iron and steel scrap. Chemical composition of individual melts was regulated alternatively by silicon carbide (SiC) or ferrosilicon (FeSi) and carburizer. The specimens from three melts of nodular cast iron with different microstructure and mechanical properties were used for experiments. Fatigue tests were realised at low frequency sinusoidal cyclic push-pull loading (stress ratio R = -1) at ambient temperature (T = 20 ± 5 °C). They were carried out with using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100 at frequency f ≈ 120 Hz.