RT Journal Article
SR Electronic
A1 Bublíková, Dagmar
A1 Mašek, Bohuslav
A1 Vorel, Ivan
A1 Jeníček, Štěpán
T1 Stability of Retained Austenite in High-Strength Martensitic Steels with Low Ms Temperature
JF Manufacturing Technology Journal
YR 2017
VO 17
IS 4
SP 428
OP 433
DO 10.21062/ujep/x.2017/a/1213-2489/MT/17/4/428
UL https://journalmt.com/artkey/mft-201704-0002.php
AB An important factor in enhancing the mechanical properties of high-strength steels is the stabilization of an appropriate amount of metastable retained austenite in martensitic matrix. Various novel heat treatment and thermomechanical processing routes have been developed recently which benefit from the effects of retained austenite in terms of achieving better elongation at still high ultimate strength levels. One of these procedures is the Q&P process (Quenching and Partitioning). It produces martensite and retained austenite to obtain strengths of more than 2000 MPa and elongation levels of about 10%. For this investigation, four steels with low Ms temperatures have been selected. Their chemistries contained manganese, silicon, molybdenum and chromium.The development of heat treatment sequences involved trials with various austenitizing temperatures, cooling rates, quenching temperatures, and carbon partitioning temperatures for the stage in which austenite becomes stabilized. The experimental heat treatment led to microstructures consisting of martensite with retained austenite in all the steels. Their strengths were in the range of 1750-2400 MPa and their A5mm elongation was 10-15 %. The largest fraction of retained austenite, according to X-ray diffraction, was 10 %. Specimens with the largest fraction of retained austenite obtained from one schedule were used for studying the stability of retained austenite under cold and hot.