PT Journal
AU Prusa, F
   Oceane, G
   Bernatikova, A
   Cygan, S
TI The Influence of SPS Compaction Pressure onto Mechanical Properties of Al-20Si-16Fe Alloy Prepared by Mechanical Alloying
SO Manufacturing Technology Journal
PY 2017
BP 936
EP 940
VL 17
IS 6
DI 10.21062/ujep/x.2017/a/1213-2489/MT/17/6/936
DE Mechanical alloying; spark plasma sintering; mechanical properties; microstructure
AB The Al-20Si-16Fe alloy (wt.%) was prepared by a combination of short-term mechanical alloying and consequential compaction via spark plasma sintering. The compaction was done at two different pressures of 80 MPa and 6 GPa to describe the influence of pressure onto a resulting properties of prepared alloy. The microstructure of both the prepared compact alloys showed presence of sub-micrometre particles embedded in the Al-matrix while some residual porosity was also observed. This corresponded to the lower compaction pressure of only 80 MPa, which, in comparison to the 6 GPa allowed to retain some porosity. The higher compaction pressure of 6 GPa resulted in a increase of the compressive strength of 1426 MPa while the hardness was slightly lower reaching still high 348 HV 5. On the other hand, the sample compacted by a pressure of 80 MPa reached compressive strength of 758 MPa while showing higher hardness of 411 HV 5. The difference in the observed properties can be attributed to a different compaction temperatures of 500°C (for 80 MPa) and of approximatelly 600°C (for 6 GPa).
ER