PT Journal
AU Knaislova, A
   Simunkova, V
   Novak, P
TI High-temperature Oxidation of Intermetallics Based on Ti-Al-Si System
SO Manufacturing Technology Journal
PY 2018
BP 255
EP 258
VL 18
IS 2
DI 10.21062/ujep/87.2018/a/1213-2489/MT/18/2/255
DE Thermal stability; Parabolic constant; Intermetallics; Reactive sintering
AB Ti-Al-Si alloys excel with their low density and good resistance against high-temperature oxidation in comparison with so far commonly used nickel alloys. Silicon in Ti-Al-Si alloys has significant positive effect on high-temperature oxidation due to increasing adhesion of oxide layer. The TiAl20Si20 alloy was evaluated as the best alloy from tested ones, because its oxide layer protected very well the basic material and TiAl20Si20 achieved good hardness after 400 hours of annealing.