RT Journal Article
SR Electronic
A1 Doluk, Elżbieta
A1 Rudawska, Anna
A1 Stančeková, Dana
A1 Mrázik, Jozef
T1 Influence of surface treatment on the strength of adhesive joints
JF Manufacturing Technology Journal
YR 2021
VO 21
IS 5
SP 585
OP 591
DO 10.21062/mft.2021.068
UL https://journalmt.com/artkey/mft-202105-0003.php
AB The article compared the strength results of single-lap adhesive joints made of galvanized steel sheet. The strength of adhesive joints was determined for two methods of surface treatment - using a degreaser (method B) and with-out a degreaser (method A). The samples were joined using a two-component epoxy adhesive based on Bisphenol A. The strength tests were carried out on a Zwick/Roell Z150 testing machine. The analysis of the surface roughness parameters of the samples for the method A was performed. The highest shear strength value (8.82 MPa) was ob-tained by method B and using P120 abrasive paper. The lowest shear strength value (4.08 MPa) was received using method A and P600 abrasive paper. The maximum values of measured surface roughness parameters were rec-orded for samples prepared with abrasive papers with granulations, respectively: P120, P220 and P180. The low-est values of Ra, Rz and Rt parameters gained using P600 abrasive paper.