PT  - JOURNAL ARTICLE
AU  - Uhríčik, Milan
AU  - Palček, Peter
AU  - Chalupová, Mária
AU  - Kuchariková, Lenka
AU  - Pastierovičová, Lucia
AU  - Medvecká, Denisa
AU  - Markovičová, Lenka
AU  - Balšianka, Róbert
AU  - Vaško, Alan
TI  - Structural and Fractographic Analysis of Aluminum Alloy before and after Fatigue Loading
DP  - 2023 Dec 6
TA  - Manufacturing Technology Journal
PG  - 725--731
VI  - 23
IP  - 5
AID - 10.21062/mft.2023.067
IS  - 12132489
AB  - The article deals with the analysis of the structure and fracture surface of aluminum alloy samples. Alu-minum alloy AlMg9 was used as an experimental material. The material from which the samples were made was supplied as cast without heat treatment, and specifically the material was produced by the continuous casting method. The structure of the test material was examined using a Neophot 32 optical microscope, and the fracture surface of the test sample was examined using a scanning electron microscope (SEM). The fatigue life of the aluminum alloy was tested by three-point bending cyclic loading using the parameters - frequency f = 100 Hz, temperature T = 22 ± 5 ℃ and stress ratio R = 0.11. The analysis showed that cast aluminum alloys are very sensitive to casting defects, such as porosity or the content and distribution of intermetallic phases. If large pores or phases are present on or near the surface of the sample, this can be the dominant cause of fatigue crack initiation and reduction of the fatigue lifetime.