T1 Effect of Filler Content and Treatment on Mechanical Properties of Polyamide Composites Reinforced with Short Carbon Fibres Grafted with Nano-SiO₂
JF Manufacturing Technology Journal
YR 2024
VO 24
IS 4
SP 521
OP 531
DO 10.21062/mft.2024.058
UL https://journalmt.com/artkey/mft-202404-0002.php
AB The polyamide PA6 composites reinforced with carbon fibres (CF) are widely studied due to their properties and their high strength to weight ratio. Good adhesion between a filler and a matrix is es-sential for enhancing properties of a resulting composite. This study investigates the effect of the short CF content and the used CF treatment on mechanical properties of the PA6-CF composites. The composites were subjected to tensile, flexural, compression, hardness and Charpy tests as well as dynamical mechanical analysis. An atomic force microscopy was employed to investigate topography of the CF and the composites. Initially, the properties of the composites were improved through the oxidation of the CF in HNO₃. Subsequently, to further enhance these properties, the oxidized CF were grafted with nano-SiO₂. The CF content in the tested composites varied from 10 wt% to 60 wt%. The most significant improvement of the tested properties was observed at the CF content of 40 wt%.