RT Journal Article
SR Electronic
A1 Vodickova, Vera
A1 Hanus, Pavel
A1 Pazourkova Prokopcakova, Petra
A1 Svec, Martin
T1 Structure Evolution of Multi-Alloyed Iron Aluminides during Two-Step Annealing
JF Manufacturing Technology Journal
YR 2024
VO 24
IS 6
SP 985
OP 991
DO 10.21062/mft.2024.099
UL https://journalmt.com/artkey/mft-202406-0009.php
AB The microstructure of single-phase (as-cast) and two-phase (after heat treatment processes) Fe3Al-based alloys doped with silicon, molybdenum, and vanadium/tungsten have been studied. The grain size and phase composition have been determined. The evolution of the secondary phase amount, morphology, and distribution during the heat treatment process has been investigated. Both alloys were heat treated at 1200°C/2 h and, subsequently, at 900 °C. For both alloys, the secondary phase formation started after heat treatment at 900°C /4h, and their amount depended on the annealing time. Vanadium atoms remain in the solid solution, while tungsten atoms partially participate in sec-ondary phase formation.