Manufacturing Technology 2013, 13(4):466-473 | DOI: 10.21062/ujep/x.2013/a/1213-2489/MT/13/4/466

The Influence of Process Fluids on the Properties of the Surface Layer of Machined Components

Jan Jersák, Lucie Vrkoslavová
Department of Machining and Assembly, Faculty of Mechanical Engineering, Technical University of Liberec

MicroScan 600-1 is a digital Barkhausen noise analyzer. It is designed for fast nondestructive surface quality control and subsurface layers of machine parts from ferromagnetic materials and for evaluating of defects which are caused by changes of residual stresses. By the instrument based on an analysis of the Barkhausen noise is determined the value of magnetoelastic parameter. Experiments which evaluated the influence of different types of process fluids to the machining process and technological properties of the machined parts from constructional steel 16MnCr (ČSN 14 220) were carried out in the laboratory of the Department of Machining and Assembly at TU in Liberec. Turned, milled and grinded test samples by using five different types of process fluids were evaluated using the analyzer. For The comparison was machining carried out also without inlet process fluid, i.e. "dry" and with the process fluid - water. Measurements of magnetoelastic parameter were performed repeatedly and measured values were statistically processed. The paper presents the resulting values of this parameter showing the influence of process fluids on the properties of the surface layer of the machined parts.

Keywords: machining, process fluids, surface integrity, magnetoelastic parameter

Published: December 1, 2013  Show citation

ACS AIP APA ASA Harvard Chicago IEEE ISO690 MLA NLM Turabian Vancouver
Jersák J, Vrkoslavová L. The Influence of Process Fluids on the Properties of the Surface Layer of Machined Components. Manufacturing Technology. 2013;13(4):466-473. doi: 10.21062/ujep/x.2013/a/1213-2489/MT/13/4/466.
Share...
Download citation
  • BibTeX (.bib)
  • Bookends (.ris)
  • EasyBib (.ris)
  • EndNote (.enw)
  • EndNote 8 (.xml)
  • ISI WoS (.isi)
  • Medlars (.medlars)
  • Mendeley (.ris)
  • MODS (.xml)
  • Papers (.ris)
  • RefWorks (.txt)
  • RefManager (.ris)
  • RIS (.ris)
  • MS Word (.xml)
  • Zotero (.ris)
    • Open article abstract

    References

    1. POPOV, Alexey, LICEK, Roman. The influence of process fluids from PARAMO a. s. on the surface roughness in turning. Strojírenská technologie, 2012, roč. XVI, č. 1 a 2, s. 60 - 64. ISSN 1211-4162.
    2. MALEC, Jiří. Některé příliš neznámé pojmy. Strojírenská technologie, 2006, roč. XI., č. 3, s. 4-5. ISSN 1211-4162.
    3. HOLEŠOVSKÝ, František. Stanovení zbytkových napětí v povrchu po obrábění. Strojírenská technologie, 2006, roč. XI, č. 3, s. 29-32. ISSN 1211-4162.
    4. VRKOSLAVOVÁ, Lucie, BAKALOVÁ, Totka. Hodnocení zbytkových napětí metodou analýzy Barkhausenova šumu v porovnání s RTG difrakcí. Jemná mechanika optika, 2013, roč. 58, č. 1, s. 11-13. ISSN 0447-6441.
    5. OCHODEK, Vladislav. Využití Barkhausenova šumu ke kontrole a optimalizaci procesu broušení. Strojírenská technologie, 2006, roč. XI., č. 3, s. 17-21. ISSN 1211-4162.
    6. GUPTA, H., ZHANG, M., PARAKKA, A. P., Barkhausen effect in ground steels. Acta Materialia, 1997, roč. 45, č. 5, s. 1917-1921, ISSN 1359-6454. Go to original source...
    7. STEWART, D. M., STEVENS, K. J., KAISER, A. B. Magnetic Barkhausen noise analysis of stress in steel. Current Applied Physics, 2004, č. 4, s. 308-311, ISSN 1567-1739. Go to original source...
    8. BUMBÁLEK, Bohumil, MALEC, Jiří. Dokončovací operace a jejich význam pro funkci součástí. Strojírenská technologie, 2006, roč. XI., č. 3, s. 25-28. ISSN 1211-4162.
    9. MÁDL, J. Vliv řezných kapalin na obráběcí proces a metodika jejich testování. In: Reotrib 2000. 1. vyd. Praha: Vysoká škola chemicko-technologická, 2000, s. 93-102, ISBN 80-7080-381-9.
    10. BUMBÁLEK, L., Zbytková napětí určovaná pomoci Barkhausenova šumu. Strojírenská technologie, 2004, roč. IX, č. 3, s. 11-15, ISSN 1211-4162.
    11. MÁDL, J., HOLEŠOVSKÝ, F., aj. Integrita obrobených povrchů z hlediska funkčních vlastností. 1. vyd. Ústí nad Labem: UJEP, FVTM, Ústí nad Labem, 2008. 230 s. ISBN 978-80-7414-095-2.
    12. ČUBAN, J., CALONIUS, O., PIETOLA, M., JERSÁK, J. Fatigue life and surface integrity measurements of S355J2 steel used in hydraulic components. Manufacturing Technology, Vol. 11, December 2011, č. -. s. 5 - 11. ISSN 1213-2489, ISBN 978-80-7414-415-8. Go to original source...
    13. GANEV, N., KOLAŘÍK, K., BLÁHOVÁ O., JERSÁK, J. Characteristics of Surface Integrity and Tribological Behaviour of Hardened Steels. Materials Engineering Vol. 16 (2009), No. 3a, pp. 68 - 72, ISSN 1335-0803.
    14. JERSÁK, J., GANEV, N., KOVALČÍK, J., DVOŘÁČKOVÁ, Š., KARÁSEK, J., HOTAŘ, A. Surface integrity of hardened bearing steel after milling. Manufacturing Technology, roč. 10, December 2010, č. -. s. 80 - 87. ISSN 1213-2489, ISBN 978-80-7414-325-0. Go to original source...
    15. PALA, Z., GANEV, N., KOLAŘÍK, K., BLÁHOVÁ, O., JERSÁK, J. Surface integrity and tribological behaviour of hardened steels. Chemické listy. roč. 105, 2011, č. 17. s. 739 - 742. ISSN 0009-2770.
    16. JERSÁK, J., REJZEK, M. Účinek procesní kapaliny na proces soustružení a vybrané parametry integrity povrchu. Strojírenská technologie, roč. 16, duben 2011, č. 2. s. 17 - 23. ISSN 1211-4162.

    Return to the content