Stability of Ni / TiB2 Coating on CuCrZr Electrodes for Resistance Spot Welding Galvanized Steel Sheet
- Faculty of Mechanical Engineering, Slovak University of Technology in Bratislava, Pionierska 15, 831 02 Bratislava
Under the influence of heat load and Zn diffusion in resistance spot welding of galvanized steel sheets, significant changes occur on the contact area of CuCrZr welding electrodes which lead to their erosion damage. Changes, causing wear of electrodes not only affect the welding process but also the quality and properties of the weld. Apart from the traditional solution (for example, the so-called "Slope" welding current) the wear of the contact surfaces can be affected by using the barrier layers - coatings. Main goal for the use of material barrier is to minimize the structural changes caused by Zn diffusion, erosion and higher heat resistance of the electrode. Recent studies have shown that such a suitable coating is a multilayer system (Ni/TiB2).
This paper is focused on the assessment of changes in the contact area of the electrodes and the barrier layer Ni / TiB2 after compila-tion 0, 1, 5, 20 and 100 welds on galvanized steel sheets type HX220BD Z100MBO.
Keywords: Resistance Spot Welding, Electro spark deposition, welding electrode, barrier coating
Published: September 1, 2017 Show citation
ACS | AIP | APA | ASA | Harvard | Chicago | IEEE | ISO690 | MLA | NLM | Turabian | Vancouver |
References
- MEŠKO, J., ZRAK, A., MULCZYK, K., TOFIL, S. (2014). Microstructure analysis of welded joints after laser welding. Manufacturing Techology: journal of science, research and production, Vol. 14, No. 3, ISSN 1213-2489.
Go to original source...
- KVASNICOVÁ, P., NOVÁK, V., NOVÁK, D., (2016). Computer Simulation of Laser Welding Technology of Chrome-Nickel Steels in Automotive Industry and its Verification by Means of Electron Microscopy. Manufacturing Techology: journal of science, research and production, Vol. 16, No.5, ISSN 1213-2489.
Go to original source...
- JAŠČÁK, Ľ., BREZINOVÁ J., HALAMA M., VIŇÁŠ J. (2011). Quality Evaluation of Resistance Spot Welds of Hot-Dip Galvanized Sheets In Corrosive Enviroment., Chemické listy, Vol. 105., No. 17, pp.709-712, ISSN 0009-2770.
- BROŽEK, M., (2016). Resistance Spot Welding of Steel Sheets. Manufacturing Techology: journal of science, research and production, Vol. 16, No. 4, ISSN 1213-2489.
Go to original source...
- DE, A., DORN, L., GUPTA, O. (2000). Analysis and Optimisation of Electrode Life for Conventional and Compound Tip Electrodes During Resistance Spot Welding of Electrogalvanised Steels, Sci. Technol. Weld. Join. Vol. 5.
Go to original source...
- HOWE, P a KELLY, S C. (1988) A comparison of the resistance spot weldability of bare,hot-dipped, galvannealed, and electrogalvanized DQSK sheet steels., International Congress and Exposition.
Go to original source...
- GEDEON, S.A. A EAGAR, T.W., (1986). Resistance Spot Welding of Galvanized Steel: Part I. Material Variations and Process Modifications., Metalurgical Transactions B, Vol. 17B.
Go to original source...
- JAŠKO, P., SEJČ, P. A BAKSA, P. (2015). Štúdium zmien na povrchu zvarových spojov a elektród s povlakom Ni/TiB2 pre odporové bodové zváranie pozinkovaných oceľových plechov., Zváranie, Vol. 63, No. 11-12, ISSN 0044-5525
- VW 01105-1., (2007). Odporové bodové zváranie. Konštrukcia. Výpočet. Nepovrstvené a povrstvené plechy
- MCLEOD, A. D., HAGGERTY, D. R. A SADOWAY, D. R. (1984). Electrical resistivites of Monocrystalline and Polycrystalline TiB2., Journal of the American ceramic Society, Vol. 67, No. 11, pp.705-708.
Go to original source...
- ZHIGANG, HOU, ILL-SOO, K., YUANXUN, W., CUNZHI, L., CHUANYAO CH. (2007). Finite element analysis for mechanical features of resistance spot welding process. Journal of Materials Processing Technology, Vol. 185
- MOSHAYEDI, H. A SATTARI-FAR, I. (2013). Resistance spot welding and the effects of welding time and current. Mechanical Engineering Department, Amirkabir University of Technology.
Go to original source...