The modification of surface of barrels by gas nitriding

Zdenek Pokorny, David Dobrocky, Zdenek Joska

Faculty of Military Technology, University of Defence, Kounicova 156/65, 662 10 Brno, Czech Republic

Steels which are used for manufacturing of highly stressed parts of military equipments such as barrels of small arms weapons must be modified by heat treatment due to achieve required mechanical properties. Moreover, other important properties of functional parts, especially a friction coefficient and surface pa-rameters of bore of barrels, must be optimized due to obtain the best accuracy in target and to increase the life time of barrel [1, 2]. The technology chromium plating, very widespread in the past, has been gradually replacing by more ecological nethods. This article is devoted to find a technology as a replacement of tradi-tional chromium plating. Experiments are focused on using of optimized gas nitriding processes for surface treatment. As a result, a higher surface hardness with low influence on the dimensional accuracy is expected. Gas nitriding process was applied to steels 42CrMo4 and 32CrMoV12-10 used for barrel manufacturing. The most important parts of barrel were evaluated, especially surface parameters as a morphology than chemical composition and naturaly a microstructure of the material. The analysis of surface morphology were performed by scanning electron microscopy; chemical composition was evaluated by GDOES method and mechanical properties by using microhardness methods. The measurements of depth of diffusion layer were performed by destructive and non-destructive methods. The measurements showed the influences of chemical composition of alloying elements in core of material after chemical-heat treatment process on depth of diffusion and influence of technology on development of porosity. All fundamental mechanical prop-erties significant for requiring function of barrel were documented [1, 2]. Nevertheless, the main task was the description of the porosity development in compound layer after gas nitriding and the increasing of sur-face hardness and the depth of diffusion layer according to chemical composition. Nitriding process was ap-plied for increasing of surface hardness of material in depth and improving of mechanical properties. Me-chanical properties of tested material were significantly increased.

Keywords: nitriding; microhardness; nitrided layer; porosity, non-destructive testing

Grants and funding:

The project The Development of Technologies, De-sign of Firearms, Ammunition, Instrumentation, Engineering of Materials and Military Infrastructure "VÝZBROJ (DZRO K201)" and “Surface technology in applications special techniques SV19-216”.

Received: September 4, 2020; Revised: December 6, 2020; Accepted: December 7, 2020; Prepublished online: December 11, 2020; Published: December 23, 2020  Show citation