Manufacturing Technology 2023, 23(1):53-59 | DOI: 10.21062/mft.2023.001

Influence of Impurity Morphology on the Fatigue Strength of High-Purity Structural Steel Melted in an Electric Furnace

Tomasz Lipiński ORCID...
Faculty of Technical Sciences, University of Warmia and Masury in Olsztyn. Oczapowskiego 11, 10-719 Olsztyn, Poland

A modern user requires low operating costs, but also reliability from machines and technical devices. Reliability during the service life depends on the quality of construction solutions, but also largely on the quality, properties and adaptation to the working conditions used in the construction of construction materials. During the operation of technical objects, their a highly predictable wear occurs. The problem is the phenomena of premature wear and damage of elements. The causes of failure of technical facilities are usually complex and depend on many factors. They can include the human factor and the one related to the quality, selection, production and technological processes of the materials used in the construc-tion of the facility. In real technical facilities, many premature failures are caused by material fatigue, which is related to the quality and distribution of impurities in the material. The paper presents the change in fatigue strength for rotational bending of low-carbon structural steel hardened and tempered at different temperatures as the effect of the size and distance between impurities on the fatigue strength of high-quality carbon structural steel melted in the industrial conditions in an electric arc furnace.

Keywords: Steel, Structural Steel, Fatigue Strength, Impurities, Arc Furnace

Received: July 12, 2022; Revised: December 13, 2022; Accepted: January 13, 2023; Prepublished online: April 24, 2023; Published: May 3, 2023  Show citation

ACS AIP APA ASA Harvard Chicago IEEE ISO690 MLA NLM Turabian Vancouver
Lipiński T. Influence of Impurity Morphology on the Fatigue Strength of High-Purity Structural Steel Melted in an Electric Furnace. Manufacturing Technology. 2023;23(1):53-59. doi: 10.21062/mft.2023.001.
Share...
Download citation
  • BibTeX (.bib)
  • Bookends (.ris)
  • EasyBib (.ris)
  • EndNote (.enw)
  • EndNote 8 (.xml)
  • ISI WoS (.isi)
  • Medlars (.medlars)
  • Mendeley (.ris)
  • MODS (.xml)
  • Papers (.ris)
  • RefWorks (.txt)
  • RefManager (.ris)
  • RIS (.ris)
  • MS Word (.xml)
  • Zotero (.ris)
    • Open full article

    References

    1. HREN, I., MICHNA, ©., NOVOTNĘ, J., MICHNOVÁ, L. (2021). Comprehensive analysis of the coated component from a FORD engine. In: Manufacturing Technology, Vol. 21, No. 4, pp. 464 - 470. ISSN 1213-2489, 2787-9402. Go to original source...
    2. LENKOVSKIY, T.M., KULYK, V.V., DURIAGINA, Z.A., KOVALCHUK, R.A., TOPILNYTSKYY, V.H., VIRA, V.V., TEPLA, T.L. (2017) Mode I and mode II fatigue crack growth resistance characteristics of high tempered 65G steel. In: Archives of Materials Science and Engineering, Vol. 84, No. 1, pp. 34 - 41. ISSN 1897-2764, 2300-8679. Go to original source...
    3. JOPEK, M. (2021). Determination of Carbon Steel Dynamic Properties. In: Manufacturing Technology, Vol. 21, No. 4, pp. 479 - 482. ISSN 1213-2489, 2787-9402. Go to original source...
    4. IVANYTSKYJ, Y.L., LENKOVSKIY, T.M., MOLKOV, Y.V., KULYK, V.V., DURIAGINA, Z.A. (2016). Influence of 65G steel microstructure on crack faces friction factor under mode fatigue fracture. In: Archives of Materials Science and Engineering, Vol. 82, No. 2, pp. 49 - 56. ISSN 1897-2764, 2300-8679. Go to original source...
    5. BLIKHARSKYY, Z., BRÓZDA, K., SELEJDAK, J. (2018). Effectivenes of Strengthening Loaded RC Beams with FRCM System. In: Archives of Civil Engineering, Vol. 64 No. 3, pp. 3 - 13. ISSN 1230-2945, 2300-3103. Go to original source...
    6. KOVÁÈIKOVÁ, P., DUBEC, A., KURICOVÁ, J. (2021). The microstructural study of a damaged motorcycle gear wheel. In Manufacturing Technology, Vol. 21, No 1, pp. 83 - 90. ISSN 1213-2489, 2787-9402. Go to original source...
    7. ADAMCZYK, M., NIŻNIK-HARAŃCZYK, B., POGORZAŁEK, J. (2016). Influence of steel smelting technology with the addition of 3 / 5% Al alloy on the type and morphology of non-metallic inclusions. In: Works of the Iron Metallurgy Institute (in Polish), Vol. 68, No. 2, pp. 24 - 32. ISSN 2657-747X.
    8. SZCZOTOK, A., PIETRASZEK, J., RADEK, N. (2017). Metallographic Study and Repeatability Analysis of γ' Phase Precipitates in Cored, Thin-Walled Castings Made from IN713C Superalloy. In: Archives of Metallurgy and Materials, Vol. 62, No. 2, pp. 595-601. ISSN 1733-3490, 2300-1909. Go to original source...
    9. KALISZ, D., MIGAS, P., KARBOWNICZEK, M., MOSKAL, M., HORNIK, A. (2020). Influence of selected deoxidizers on chemical composition of molten inclusions in liquid steel. In: Journal of Materials Engineering and Performance, Vol. 29, No. 3, pp. 1479 -1487. ISSN 1059-9495, 1544-1024. Go to original source...
    10. WOŹNY, A. (2020). Selected problems of managing work safety-case study. In: Production Engineering Archives, Vol. 26, No. 3, pp. 99 - 103. ISSN 2353-7779. Go to original source...
    11. GULYAKOV, V.S., VUSIKHIS, A. S., KUDINOV, D. Z. (2012). Nonmetallic Oxide Inclusions and Oxy-gen in the Vacuum_Jet Refining of Steel. In: Steel in Translation, Vol. 42, No. 11, pp. 781 - 783. ISSN 0967-0912. Go to original source...
    12. KRYNKE, M. (2021) Management optimizing the costs and duration time of the process in the production system. In: Production Engineering Archives, Vol. 27, No. 3, pp. 163 - 170. ISSN 2353-7779. Go to original source...
    13. LIPIŃSKI, T., WACH, A. (2014). Influence of outside furnace treatment on purity medium carbon steel. In: METAL 2014 - 23rd International Conference on Metallurgy and Materials, Conference Proceedings, pp. 738-743. ISSN 2694-9296.
    14. ROIKO, A., HÄNNINEN, H., VUORIKARI, H. (2012). Anisotropic distribution of non-metallic inclusions in forged steel roll and its influence on fatigue limit. In: International Journal of Fatigue, Vol. 41, pp.158-167. ISSN 0142-1123, 1879- 3452. Go to original source...
    15. LIPIŃSKI, T. (2018). The effect of the diameter and spacing between impurities on the fatigue strength coefficient of structural steel. In: Archives of Metallurgy and Materials, Vol. 63, No. 1, pp. 519 - 524. ISSN 1733-3490, 2300-1909. Go to original source...
    16. LIPIŃSKI, T., WACH, A. (2015). Effect Size Proportions and Distances Between the Non-metallic Inclusions on Bending Fatigue Strength of Structural Steel. In: 24td International Conference on Metallurgy and Materials Metal 2015 Brno TANGER Ltd., Ostrava. Conference proceedings (2015) pp. 754 - 760. ISSN 2694-9296.
    17. BRICÍN, D., KŰÍź, A. (2021). Influence of the Boriding Process on the Properties and the Structure of the Steel S265 and the Steel X6CrNiTi18-10. In: Manufacturing Technology, Vol. 21, No. 1, pp. 37 - 44. ISSN 1213-2489, 2787-9402. Go to original source...
    18. DONG, Z., QIAN, D., YIN, F., WANG, F. (2021). Enhanced Impact Toughness of Previously Cold Rolled High-Carbon Chromium Bearing Steel with Rare Earth Addition. In: Journal of Materials Engineering and Performance, 30(11), 8178 - 8187. ISSN 1059-9495, 1544-1024. Go to original source...
    19. CZAJKOWSKA, A., INGALDI, M. (2022). Influence of Steel Fibers Content on Selected Mechanical Properties - Experimental Tests. In: Manufacturing Technology, Vol. 22, No. 3, pp. 267 - 278. ISSN 1213-2489, 2787-9402. Go to original source...
    20. WANG, X. (2017). Study on Rolling Process and Fatigue Performance of Hot Rolled High Strength Steel for Wheel. In: Chemical Engineering Transactions, Vol. 59, pp. 229 - 234. ISSN 2283-9216.
    21. CHUBUKOV, M.Y., RUTSKIY, D.V., USKOV, D.P. (2019). Analyzing the features of non-metallic inclusion distribution in Ø410 mm continuously cast billets of low carbon steel grades. In: Materials Science Forum, Vol. 973, pp. 21 - 25). Trans Tech Publications Ltd. ISSN 0255-5476. Go to original source...
    22. CHAN, K.S. (2010). Roles of microstructure in fatigue crack initiation. In: International Journal of Fatigue, Vol. 32, pp. 1428 - 1447. ISSN 0142-1123, 1879- 3452. Go to original source...
    23. RADEK, N., TOKAR, D., KALINOWSKI, A., PIETRASZEK, J. (2021). Influence of laser texturing on tribological properties of DLC coatings. In: Production Engineering Archives, vol.27, no.2, pp.119 - 123. ISSN: 23535156. Go to original source...
    24. LIPIŃSKI, T. (2017). Roughness of 1.0721 steel after corrosion tests in 20% NaCl. In: Production Engineering Archives, Vol. 15, No. 15, pp. 27 - 30. ISSN 2353-7779. Go to original source...
    25. ULEWICZ, R., SZATANIAK, P., NOVY, F. (2014). Fatigue properties of wear resistant martensitic steel. In: METAL 2014 - 23rd International Conference on Metallurgy and Materials, Conference Proceedings, pp. 784 - 789. ISSN 2694-9296.
    26. XIAO-FEI, H., CHENG-FEI, H., LE, X., MAO-QIU, W. (2021). Effect of total oxygen on the nonmetallic inclusion of gear steel. In: Chinese Journal of Engineering, Vol. 43, No. 4, pp. 537 - 544. ISSN 2095-9389.
    27. BLIKHARSKYY, Y., SELEJDAK, J., KOPIIKA, N. (2021). Corrosion fatigue damages of rebars under loading in time. In: Materials, Vol. 14, No. 12, pp. 3416. ISSN 2053-1583. Go to original source...
    28. MACEK, W., SZALA, M., TREMBACZ, J., BRANCO, R., COSTA, J. (2020). Effect of non-zero mean stress bending-torsion fatigue on fracture surface parameters of 34CrNiMo6 steel notched bars, In: Pro-duction Engineering Archives, Vol. 26, No. 4, pp. 167 - 173. ISSN 2353-7779. Go to original source...
    29. HUA L., DENG S., HAN X., HUANG S. (2013). Effect of material defects on crack initiation under rolling contact fatigue in a bearing ring. In: Tribology International, Vol. 66, pp. 315 - 323. ISSN 0301-679X 1879-2464. Go to original source...
    30. QAYYUM, F., UMAR, M., ELAGIN, V., KIRSCHNER, M., HOFFMANN, F., GUK, S., PRAHL, U. (2022). Influence of non-metallic inclusions on local deformation and damage behavior of modified 16MnCrS5 steel. In: Crystals, Vol. 12, No. 2, pp. 281. ISSN 2073-4352. Go to original source...
    31. LIPIŃSKI, T., WACH, A. (2015). The effect of fine non-metallic inclusions on the fatigue strength of structural steel Terms and conditions. In: Archives of Metallurgy and Materials, Vol. 60, No. 1, pp. 65 - 69. ISSN 1733-3490, 2300-1909. Go to original source...
    32. LIPIŃSKI, T., WACH, A., (2015). Effect of the impurities on the bending fatigue strength of structural steel. In: 14th International Scientific Conference Engineering for Rural Development Proceedings vol. 14, Jelgava, 20.-22.05.2015, pp. 784 - 789. ISSN 1691-5976.
    33. LIPIŃSKI, T., ULEWICZ, R. (2021). The effect of the impurities spaces on the quality of structural steel working at variable loads. In: Open Engineering, Vol. 11, No. 1, pp. 233 - 238. ISSN 2391-5439. Go to original source...
    34. HALFORD, G.L. (1986). Low cycle thermal fatigue. NASA.
    35. SRIVASTAVA, A., PONSON, L., OSOVSKI, S., BOUCHAUD, E., TVERGAARD, V., NEEDLEMAN, A. (2014). Effect of inclusion density on ductile fracture toughness and roughness. In: Journal of the Mechanics and Physics of Solids Vol. 63, pp. 62 - 79.ISSN 0022-5096, 1873-4782. Go to original source...
    36. LIPIŃSKI, T. (2015). Effect of the spacing between submicroscopic oxide impurities on the fatigue strength of structural steel. In: Archives of Metallurgy and Materials, Vol. 60, No. 3B, pp. 2385 - 2390. ISSN 1733-3490, 2300-1909. Go to original source...
    37. MURAKAMI, Y. (2002). Metal fatigue. Effects of small defects and inclusions. Elsevier.
    38. MURAKAMI, Y., NOMOTO, T., UEDA, T. (1999). Factors influencing the mechanism of super long fatigue failure in steels. In: Fatigue & Fracture of Engineering Materials & Structures, Vol. 22, pp.581-590. Go to original source...
    39. MURAKAMI, Y., KODAMA, S., KONUMA, S. (1989). Quantitative evaluation of effects of non-metallic inclusions on fatigue strength of high strength steels, I: basic fatigue mechanism and fatigue fracture stress and the size and location of non-metallic inclusions, International Journal of Fatigue, Vol. 11, No. 5, pp. 291-298. ISSN 0142-1123, 1879-3452. Go to original source...
    40. GU, C., LIU, W.Q., LIAN, J.H., BAO, Y.P. (2021). In-depth analysis of the fatigue mechanism induced by inclusions for high-strength bearing steels. In: International Journal of Minerals Metallurgy and Materials Vol. 28, No 5, pp. 826-834. ISSN 1674-4799. Go to original source...
    41. MALASHCHENKO, V., STRILETS, O., STRILETS, V., KŁYSZ, S. (2019). Investigation of the energy effectiveness of multistage differential gears when the speed is changed by the carrier. Diagnostyka, Vol. 20, No. 4, pp. 57 - 64. ISSN 1641-6414. Go to original source...
    42. FOLETTI S., BERETTA S., TARANTINO M.G. (2014). Multiaxial fatigue criteria versus experiments for small crack under rolling contact fatigue, In: International Journal of Fatigue, Vol. 58, pp. 181 - 182. ISSN 0142-1123, 1879-3452. Go to original source...
    43. SHI, Z.Y., LI, J.J., ZHANG, X.D., SHANG, C.J., CAO, W.Q. (2022). Influence Mechanisms of Inclusion Types on Rotating Bending Fatigue Properties of SAE52100 Bearing Steel. In: Materials, Vol. 15, No 14, Article Number 5037. ISSN 2053-1583. Go to original source...
    44. MITCHELL, M.R. (1996). Fundamentals of Modern Fatigue Analysis for Design. Fatigue and Fracture, Vol. 19, ASM Handbook, ASM International. Go to original source...
    45. EVANS, M.H., RICHARDSON, A.D., WANG, L., WOOD, R.J.K., ANDERSON, W.B. (2014). Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation. In: Tribology International Vol. 75, pp. 87 - 97. ISSN 0301-679X 1879-2464. Go to original source...
    46. LIPIŃSKI, T., WACH, A. (2020). Influence of inclusions on bending fatigue strength coefficient the medium carbon steel melted in an electric furnace. In: Production Engineering Archives Volume 26, Issue 3, pp. 88 - 91. ISSN: 23535156. Go to original source...
    47. LIPIŃSKI, T. (2018). Bending fatigue strength coefficient the low carbon steel with impurities. In: Production Engineering Archives, Vol. 21, No. 21, pp. 20 - 23. ISSN 2353-7779. Go to original source...
    48. CUARTAS, M., RUIZ, E., FERREÑO, D., SETIÉN, J., ARROYO, V., GUTIÉRREZ-SOLANA, F. (2021). Machine learning algorithms for the prediction of non-metallic inclusions in steel wires for tire reinforcement. In: Journal of Intelligent Manufacturing, Vol. 32, No. 6, pp. 1739 - 1751. ISSN 0956-5515, 1572-8145. Go to original source...
    49. PIETRASZEK, J., GĄDEK-MOSZCZAK, A., RADEK, N. (2014). The estimation of accuracy for the neural network approximation in the case of sintered metal properties. Studies in Computational Intelligence, Vol. 513, pp. 125 - 134. ISSN 1860-949X. Go to original source...
    50. SURESH, S. (1998). Fatigue of Materials. Cambridge University Press: Cambridge, UK. ISBN 9780511806575. Go to original source...

    This is an open access article distributed under the terms of the Attribution-NonCommercial 4.0 International License (CC BY-NC 4.0), which permits non-comercial use, distribution, and reproduction in any medium, provided the original publication is properly cited. No use, distribution or reproduction is permitted which does not comply with these terms.


    Return to the content