The Overview of Intermetallic Phases Presented in Nickel Base Superalloys after Precipitation Hardening

Juraj Belan, Lenka Kuchariková, Eva Tillová, Milan Uhríčik

Faculty of Mechanical Engineering, University of Žilina. Univerzitná 8215/1, 010 26 Žilina. Slovakia

The nickel base superalloys are progressive group of materials designed especially for application where others materials does not fit with its mechanical properties (such aluminium or copper alloys) or corrosion resistance at high temperature nor heat-temperature properties (such iron or steel). Their unique properties comes from solid solution gamma, where after precipitation hardening a various phases - γ' (gamma prime), γ'' (gamma double prime), δ (delta), different types of carbides (MC, M23C6, M6C, and M7C3) with various degree of coherency to matrix are presented. Article gives a brief description of such phases with its affect to mechanical properties.

Keywords: Ni-based superalloys, gamma prime phase, gamma double prime phase, delta phase, metallography evaluation, SEM observation

Published: September 1, 2015  Show citation